PROPERTIES OF NON-BLACK COMPOUNDS |
 |
| Description:
Specific compounding ingredients
can reduce or eliminate the presence of
carbon black. These compounds may provide
improved resistance to oxidative environments
and reactive plasmas. The inorganic pigments
are not recommended for use in wet chemical
environments as they have been shown to
increase the extractable ionic contamination.
Chemistry: The base chemistry for these compounds remains relatively unchanged from the carbon-black-filled versions of these fluoroelastomers. Most non-black fluoroelas-tomers are based on a copolymer fluoroelastomer (vinylidene fluoride and hexafluoropropylene). |
|
| ISC-FNGP Compound |
Color | Hardness (Shore A) |
Tensile Mpa (psi) |
Elongation (%) |
70hr C/S @200ÜC |
Low Temp |
High Temp |
|
| V60WH | White | 65 | 15.1 (2,190) |
220 | 8 | -25ÉC (-13ÉF) |
200ÉC (392ÉF) | <<Select |
| V75WH | White | 71 | 12.3 (1,780) |
175 | 11 | -25ÉC (-13ÉF) |
200ÉC (392ÉF) | <<Select |
| V180 | White | 76 | 15.3 (2,220) |
165 | 18 | -20ÉC (-4ÉF) |
200ÉC (392ÉF) |
<<Select |
| V75BR | Brown | 74 | 13.3 (1,930) |
180 | 15 | -25ÉC (-13ÉF) |
200ÉC (392ÉF) |
<<Select |
| V189 | Brown | 75 | 13.3 (1,930) |
180 | 15 | -20ÉC (-4ÉF) |
200ÉC (392ÉF) |
<<Select |
| V195 | Brown | 78 | 11.4 (1,650) |
205 | 15 | -20ÉC (-4ÉF) |
200ÉC (392ÉF) |
<<Select |
| V90BR | Brown | 91 | 15.3 (2,220) |
130 | 15 | -25ÉC (-13ÉF) |
200ÉC (392ÉF) |
<<Select |
| V160 | Green | 73 | 10.76 (1,540) |
190 | 12 | -20ÉC (-4ÉF) |
200ÉC (392ÉF) |
<<Select |
| V178 | Red | 76 | 15.7 (2,280) |
160 | 16 | -20ÉC (-4ÉF) |
200ÉC (392ÉF) |
<<Select |
Back